반응성 스프레이방법으로 제작한 티타늄 알루미나이드/탄화물 복합박막의 미세조직과 경도 = Microstructure and Hardness of Titanium Aluminide/Carbide Composite Coatings Prepared by Reactive Spray Method

다국어 초록 (Multilingual Abstract)

A variety of composite powders having different aluminum and carbon contents are prepared using various organic solvents having different amounts of carbon atoms in unit volume as ball milling agents for titanium and aluminum ball milling. The effects of substrate temperature and post-heat treatment on the texture and hardness of the coating are investigated by spraying with this reduced pressure plasma spray. The aluminum part of the composite powder evaporates during spraying, so that the film aluminum content is 30.9 mass%~37.4 mass% and the carbon content is 0.64 mass%~1.69 mass%. The main constituent phase of the coating formed on the water-cooled substrate is a non-planar α₂ phase, obtained by supersaturated carbon regardless of the alloy composition. When these films are heat-treated at 1123 K, the main constituent phase becomes γ phase, and fine Ti₂AlC precipitates to increase the film hardness. However, when heat treatment is performed at a higher temperature, the hardness is lowered. The main constitutional phase of the coating formed on the preheated substrate is an equilibrium gamma phase, and fine Ti₂AlC precipitates. The hardness of this coating is much higher than the hardness of the coating in the sprayed state formed on the water-cooled substrate. When hot pressing is applied to the coating, the porosity decreases but hardness also decreases because Ti₂AlC grows. The amount of Ti₂AlC in the hot-pressed film is 4.9 vol% to 15.3 vol%, depending on the carbon content of the film.

참고문헌 (Reference)

• 1 C. Bartuli, 14 : 187-, 2005
• 2 E. Sadeghi, 576 : 317-, 2013
• 3 M. Manjunatha, 5 : 622-, 2014
• 4 N. A. Allsop, 513 : 52-, 2006
• 5 Y. Sun, 45 : 2750-, 2014
• 6 H. Wang, 49 : 1639-, 2015
• 7 Z. Yang, 79 : 52-, 2013
• 8 V. Chawla, 565 : 94-, 2014
• 9 P. Bhattacharya, 368 : 187-, 2004
• 10 S. Matthews, 13 : 526-, 2004
• 11 Y. Lin, 22A : 859-, 1991
• 12 T. Cegan, 48 : 831-, 2014
• 13 G. C. Wang, 762 : 607-, 2013
• 14 M. Hasan, 202 : 4006-, 2008
• 15 Y. L. Chen, 690-693 : 643-, 2013
• 16 S. Rech, 94 : 69-, 2013
• 17 Z. Feng, 31 : 1193-, 2015
• 18 S. R. Kulkarni, 490 : 155-, 2010
• 19 Robert W. Cahn, "Ternary Alloys : A Comprehensive Compendium of Evaluated Constitutional Data and Phase Diagrams" VCH Verlagsgeselshaft,VCH Publications 557-, 1990
• 20 A. H. Johnstone, "Handbook of Chemistry and Physics" CRC Press C-105-, 1988