계룡산 석간주를 사용한 흑색 안료 개발 = Development of Black Pigment Using Seokganju of Mountain Gyeryong

다국어 초록 (Multilingual Abstract)

We collected Seokganju minerals (regions in Gyeryong Mountain, Sangsin-ri, Banpo-myeon, Gongju Chungcheongnam-province), which were used as natural color pigments for grayish-blue during the 15th~16th centuries of the Joseon era, and investigated their crystallographic features to develop a black pigment having a spinel structure. By a Raman analysis, the color of Seokganju under transparent glaze as a pigment for painting was black because hematite ($Fe_2O_3$) in Seokganju was converted to magnetite ($Fe_3O_4$) However, Seokganju into the transparent glaze as a pigment was brown because of hematite ($Fe_2O_3$) and small amounts of maghemite (${\gamma}-Fe_2O_3$) in Seokganju minerals. Only Seokganju mineral is used, it is not suitable for black pigment into the transparent glaze. This study tried to develop a spinel crystal black pigment stabilized by Seokganju with CoO, $Cr_2O_3$, NiO, and $MnO_2$ at $1280^{\circ}C$. A Raman spectroscopy analysis was performed to verify the presence of Mn The results showed that it existed as spinel, and two crystal phases $CoFe_2O_4$ and $MnFe_2O_4$ were mixed. $CoFe_2O_4$ spinel has a dark grayish black color and $MnFe_2O_4$ spinel has a greenish black color, and these two appeared as black. The color of a specimen calcined by adding 6 wt% of pigment mixed with 5 wt% of $MnO_2$ added to lime glaze was analyzed with a UV spectrophotometer. When applying the color pigment, it appeared black stabilized with $L^*$24.23, $a^*$ 0.12, $b^*$ -2.29 at $1260^{\circ}C$ oxidative calcination, With $1240^{\circ}C$ reduction firing, it is appeared black stabilized with low brightness of $L^*$ 23.13, $a^*$ -1.12, $b^*$ 0.54.

참고문헌 (Reference)

• 1 S. H. Lim, Myongji University 2003
• 2 K. R. Pyon, Myongji University 2010
• 3 S. N. Choi, Myongji University 2007
• 4 이광호, "고온용 검정색 스피넬 안료의 개발" 한국세라믹학회 44 (44): 160-165, 2007
• 5 황동하, "ZrTiO4계 Gray 안료 합성과 형성기구" 한국세라믹학회 49 (49): 84-89, 2012
• 6 G. V. M. Jacintho, "Structural Investigation of MFe2O4(M = Fe, Co) Magnetic Fluids" 113 (113): 7684-7691, 2009
• 7 M. Handesch, "Raman spectroscopy of Iron Oxides and (oxy)Hydroxides at Low Laser Power and Possible Applications in Environmental Magnetic Studies" 177 (177): 941-948, 2009
• 8 L. B. Gurlet, "Raman Studies of Corrosion Layers Formed on Archaeological Irons in Various Media" 8 : 147-156, 2009
• 9 O. N. Shebanova, "Raman Spectroscopic Study of Magnetite (FeFe2O4): a New Aassignment for the Vibrational Spectrum" 174 (174): 424-430, 2003
• 10 임성호, "Image Cut Raman Microscope을 사용한 계룡산 철화 분청사기 연구" 한국세라믹학회 47 (47): 312-318, 2010
• 11 Y. Shiraki, "Glaze and Pigment" Deakwang 684-, 1980