In this study, in the selection of materials for the elements of a small plant, those with high resistance to corrosion are selected and the material properties of coatings for corrosion prevention are evaluated. In addition, corrosion characteristics and material analysis were performed on the welded part, and the hardness characteristics of the welded part, heat-affected part, and the base metal were evaluated. In the case of the post-weld-heat-treated(PWHT) specimen, the corrosion resistance of STS 316 was lower than that of the specimen without the PWHT due to the formation of intergranular carbide. As a result of evaluating the distribution of the hardness of the weld before and after the PWHT, the hardness of the specimen after the PWHT increased by about 20 Hv. As a result of the corrosion test on the welded specimen, the weight loss tended to increase as the time increased. In the case of the PWHT specimen, the corrosion resistance tended to be significantly lower than that of the specimen without PWHT due to the formation of intergranular carbide.