타타늄의 열처리 조건에 따른 동전위 양극분극특성 및 표면 미세구조 변화 = Effect of Heat Treatment Conditions on Dynamic Anodic Polarization Characteristics and Surface Microstructure of Titanium
저자
주동현 (전남대학교 치과대학 치과재료학교실 및 치과재료연구소) ; 이용렬 (전남대학교 치과대학 치과재료학교실 및 치과재료연구소) ; 정영화 (전남대학교 치과대학 치과재료학교실 및 치과재료연구소) ; 양홍서 (전남대학교 치과대학 보철학학교실 ) ; 박상원 (전남대학교 치과대학 보철학학교실 ) ; 박영준 (전남대학교 치과대학 치과재료학교실 및 치과재료연구소) ; 이도재 (전남대학교 공과대학 신소재공학부) ; 송호준 (한국기초과학지원연구원)
발행기관
학술지명
대한치과재료학회지(THE JOURNAL OF THE KOREA RESEARCH SOCIETY FOR DENTAL MATREIALS)
권호사항
발행연도
2002
작성언어
Korean
주제어
KDC
515.12
등재정보
KCI등재
자료형태
학술저널
발행기관 URL
수록면
145-156(12쪽)
제공처
The corrosion resistance of metallic implants is essential for successful implant osseointegration. Moreover, the implant surface should have appropriate surface roughness for the attachment of the osteoblast and collagen fibrils. When titanium is exposed to air a thermodynamically very stable oxide film is formed at once. This oxide is very thin and yet it protects the metal from corrosion instantaneously. However, the oxide would not be ideal, and it would be supposed that the state of oxide film would be various by the different conditions when it is formed. The objective of this study was to evaluate the electrochemical properties and surface microstructural changes of titanium after passivation treatment or exposure to high heat (in vacuum or in air).
ASTM grade 2 commercially pure titanium (Ti) disks of 10㎜ diameter were wet ground and polished with 240 and 600 grit SiC, and then ultrasonically cleaned with distilled water and ethanol. Cleansed as-received samples (As-R group) were passivated with 30% nitric acid solution at 50℃ for 15 minutes to make the Pas group. The Std-V samples were made by treating the Ti disks in vacuum quartz tube (10^-8 Torr) at 530℃ for 40 min for stress relieving, followed by annealing at 700℃ for 90 min, and then slow cooling to room temperature. The Std-A samples undergo identical procedure as the Std-V group except that it is done in air. For 530℃-V samples, Ti disks were heated at 530℃ for 40 minutes and slow cooled to room temperature. The 1000℃-V samples were produced by heating Std-V specimens again at 1000℃ for 2 hr, followed by cooling to room temperature. 530℃-A and 1000℃-A samples were also prepared.
Potentiodynamic anodic polarization measurement, SEM, AFM and XRD analysis were performed to evaluate the effects of the various treatments.
The difference in the mean values of E_corr between groups showed statistically significant difference (P<0.05), but that of I_corr did not show significance (P>0.05). When Ti surface was passivated there was a shift of corrosion potential (E_corr) in the noble direction and a lower corrosion current density (I_corr) value. Std-A samples showed most noble E_corr value among the tested groups. 530℃-V samples showed more noble E-corr than other tested groups except Std-A group. 1000℃-V samples showed more noble E-corr than those of Std-V sample. In the case of Std-, 530℃- and 1000℃-groups, -A sub-groups showed better corrosion resistant characteristics than -V sub-groups in regard to E-corr and I_corr values. In the SEM observations, the surfaces of the As-R samples showed only scratch line on smooth surface. In Pas samples, thick oxide layer covered the surface under high magnification observation. 530℃-A samples were covered by oxide granules, and Std-A samples had 25~50 nm-thick acicular oxides. The 1000℃-A samples were covered by coarse oxide crystals with a granule diameter of 0.1~0.6 μm having a gross appearance of milky white color, which was identified by XRD as a rutile. On the other hand, 1000℃-V samples showed an Widmansta¨tten structrue of which the orientation of the lattice is formed along crystallographic planes of the parent crystals. On the AFM observation, 530℃-A samples showed RMS roughness of 79.38 nm which is 5 times rougher than those of the As-R samples. Std-A sample had a roughness of 330.47 nm which is about 20-times rougher than that of the As-R sample. 1000℃-A samples were covered by coarse granular oxides and the roughness were about 0.56 μm. Vacuum sub-group samples showed a more smooth surface than air sub-group samples, and the oxide film was more dense.
Due to variability of the surface treatment and heat treatment conditions, the process of the oxide formation seems to be affected thereby making the corrosion properties and surface micro-morphology different. However, more various electrochemical analysis together with surface analysis, and an investigation for the effects of those on the osteoblast cell adhesion and calcium phosphate apposition are needed for the improvement of the osseointegration rates of the titanium implants.
분석정보
서지정보 내보내기(Export)
닫기소장기관 정보
닫기권호소장정보
닫기오류접수
닫기오류 접수 확인
닫기음성서비스 신청
닫기음성서비스 신청 확인
닫기이용약관
닫기학술연구정보서비스 이용약관 (2017년 1월 1일 ~ 현재 적용)
학술연구정보서비스(이하 RISS)는 정보주체의 자유와 권리 보호를 위해 「개인정보 보호법」 및 관계 법령이 정한 바를 준수하여, 적법하게 개인정보를 처리하고 안전하게 관리하고 있습니다. 이에 「개인정보 보호법」 제30조에 따라 정보주체에게 개인정보 처리에 관한 절차 및 기준을 안내하고, 이와 관련한 고충을 신속하고 원활하게 처리할 수 있도록 하기 위하여 다음과 같이 개인정보 처리방침을 수립·공개합니다.
주요 개인정보 처리 표시(라벨링)
목 차
3년
또는 회원탈퇴시까지5년
(「전자상거래 등에서의 소비자보호에 관한3년
(「전자상거래 등에서의 소비자보호에 관한2년
이상(개인정보보호위원회 : 개인정보의 안전성 확보조치 기준)개인정보파일의 명칭 | 운영근거 / 처리목적 | 개인정보파일에 기록되는 개인정보의 항목 | 보유기간 | |
---|---|---|---|---|
학술연구정보서비스 이용자 가입정보 파일 | 한국교육학술정보원법 | 필수 | ID, 비밀번호, 성명, 생년월일, 신분(직업구분), 이메일, 소속분야, 웹진메일 수신동의 여부 | 3년 또는 탈퇴시 |
선택 | 소속기관명, 소속도서관명, 학과/부서명, 학번/직원번호, 휴대전화, 주소 |
구분 | 담당자 | 연락처 |
---|---|---|
KERIS 개인정보 보호책임자 | 정보보호본부 김태우 | - 이메일 : lsy@keris.or.kr - 전화번호 : 053-714-0439 - 팩스번호 : 053-714-0195 |
KERIS 개인정보 보호담당자 | 개인정보보호부 이상엽 | |
RISS 개인정보 보호책임자 | 대학학술본부 장금연 | - 이메일 : giltizen@keris.or.kr - 전화번호 : 053-714-0149 - 팩스번호 : 053-714-0194 |
RISS 개인정보 보호담당자 | 학술진흥부 길원진 |
자동로그아웃 안내
닫기인증오류 안내
닫기귀하께서는 휴면계정 전환 후 1년동안 회원정보 수집 및 이용에 대한
재동의를 하지 않으신 관계로 개인정보가 삭제되었습니다.
(참조 : RISS 이용약관 및 개인정보처리방침)
신규회원으로 가입하여 이용 부탁 드리며, 추가 문의는 고객센터로 연락 바랍니다.
- 기존 아이디 재사용 불가
휴면계정 안내
RISS는 [표준개인정보 보호지침]에 따라 2년을 주기로 개인정보 수집·이용에 관하여 (재)동의를 받고 있으며, (재)동의를 하지 않을 경우, 휴면계정으로 전환됩니다.
(※ 휴면계정은 원문이용 및 복사/대출 서비스를 이용할 수 없습니다.)
휴면계정으로 전환된 후 1년간 회원정보 수집·이용에 대한 재동의를 하지 않을 경우, RISS에서 자동탈퇴 및 개인정보가 삭제처리 됩니다.
고객센터 1599-3122
ARS번호+1번(회원가입 및 정보수정)