노화에 따른 아스팔트 콘크리트 포장의 수분민감성 평가 = An Evaluation of Moisture Sensitivity of Asphalt Concrete Pavement Due to Aging

다국어 초록 (Multilingual Abstract)

Pavement distress and traffic accidents are caused by pot-hole. In addition, direct and indirect damages of road users are increasing, such as loss of life due to personal injury and damage to vehicles. Generally, the asphalt concrete pavements are continuously aging from the production process to the terminal performance period. Aging causes stripping due to cracks and moisture penetration and weakening the pavement structure to induce pot-hole. In this study, adhesion performance and moisture sensitivity were evaluated according to aging degree in order to investigate the effect of aging on asphalt pavement. As a result of the study, the viscosity of the asphalt binder was increased with aging and the bond strength of the aged was increased 2~3 times than that of the unaged. The resultsof accelerated aging test showed an increases in indirect tensile strength and the increase in the TSR (Tensile Strength Ratio) by 4.2~8.9%. As a result, it is noted that the anti-stripping and adhesion performances of the aged asphalt concrete are improved compared to the unaged one under the aging conditions of asphalt binder coated on aggregates

국문 초록 (Abstract)

포트홀 발생 및 관련 교통사고 건수는 매년 꾸준히 증가하는 추세이며 이에 따른 인명피해, 차량파손에 따른 비용손실 등 도로 이용자의 직·간접적인 피해를 증가시키고 있다. 일반적으로 아스팔트 혼합물은 생산과정부터 시공 후 공용에 따라 지속적으로 노화가 진행된다. 포장 노화는 균열과 수분침투로 박리를 야기하고 반복적인 윤하중에 의해 포장구조를 약화시켜 포트홀을 유발하게 된다. 본 연구에서는 노화가 아스팔트 콘크리트 포장에 미치는 영향을 검토하기 위해 노화정도에 따른 부착성능 평가와 수분민감성 평가를 수행하였다. 연구결과 노화에 따라 아스팔트 바인더의 점성이 증가해 부착강도가 2~3배 이상 증가하였다. 또한 가속 노화시킨 아스팔트 혼합물의 경우 간접인장강도의 증가뿐만 아니라 TSR값도 4.2~8.9 % 증가하는 것으로 나타났다. 이에 따라 골재에 아스팔트 바인더가 피복된 상태에서 노화가 진행될 경우 아스팔트 바인더와 골재의 부착력이 증가하여 박리 저항성이 향상되는 것으로 분석되었다.

참고문헌 (Reference)

• 1 김경남, "포트홀 감지 시스템을 이용한 보수재료량 산출 알고리즘 개발" 대한토목학회 37 (37): 603-610, 2017
• 2 김경남, "예방적 유지보수를 위한 아스팔트 표면강화공법의 실내 성능 평가" 대한토목학회 38 (38): 311-318, 2018
• 3 정재헌, "아스팔트 혼합물의 인공노화 방안 연구" 한국도로학회 9 (9): 45-54, 2007
• 4 이관호, "아스팔트 바인더의 노화특성을 고려한 동탄성계수 평가" 한국방재학회 8 (8): 51-58, 2008
• 5 김유석, "보일러 부산 애쉬를 이용한 아스팔트 콘크리트의 박리저항성 평가" 대한토목학회 38 (38): 319-326, 2018
• 6 Read, J., "The shell bitumen handbook" Shell Bitumen 2003
• 7 Bahia, H. U., "Testing methods to determine aggregate/asphalt adhesion properties and potential moisture damage" Wisconsin Highway Research 2007
• 8 National Assembly, "Pothole caused by the use of sub-standard materials is need to fundamental solution urgently" 2013
• 9 "KS F 2398, Standard method for resistance of compacted asphalt mixtures to moisture induced damage"
• 10 Yener, E., "Effects of exposure time and temperature in aging test on asphalt binder properties" 5 (5): 112-124, 2014
• 11 Shin, O. C., "Effect of change in adhesive and cohesive characteristics between asphalt binder and aggregate due to moisture on pavement material damage" Kyung Hee University 2017
• 12 Aguiar-Moya, J. P., "Effect of aging on adhesion properties of asphalt mixtures with the use of bitumen bond strength and surface energy measurement tests" Transportation Research Board (2505) : 57-65, 2015
• 13 Korea Institute of Civil Engineering and Building Technology, "Development of road pavement construction quality management system against climate change (2nd Final Report)" 2012
• 14 Little, D. N., "Chemical and mechanical mechanisms of moisture damage in hot mix asphalt pavements" 2003
• 15 Kim, S. W., "Characterization of asphalt mixture at the point of pothole occurrence" KSRE 27-, 2015
• 16 Jo, M. H., "Asphalt concrete pavement pothole: Repair method" 15 (15): 43-51, 2013
• 17 "ASTM D 572, Standard test method for rubber-deterioration by heat and oxygen"
• 18 "ASTM D 454, Standard test method for rubber deterioration by heat and air pressure"
• 19 "ASTM D 2872, Standard test method for effect of heat and air on a moving film of asphalt (Rolling thin-film oven test)"
• 20 "AASHTO TP 91, Determining asphalt binder bond strength by means of the Binder Bond Strength (BBS) test"
• 21 "AASHTO T 283, Standard method of test for resistance of compacted asphalt mixtures to moisture-induced damage"
• 22 "AASHTO T 240, Standard method of test for effect of heat and air on a moving film of asphalt binder (Rolling thin-film oven test)"