Development of body formulations using colemanite waste in porcelain tile production
저자
Nezahat Ediz (Dumluplnar University) ; Arife Yurdakul (Bruno Seramik)
발행기관
학술지명
권호사항
발행연도
2009
작성언어
English
주제어
등재정보
KCI등재,SCIE,SCOPUS
자료형태
학술저널
수록면
758-769(12쪽)
KCI 피인용횟수
8
DOI식별코드
제공처
Porcelain tiles have become one of the most important products of the ceramic industry in the last decade mainly owing to
their attractive physical and mechanical properties including high strength, high fracture toughness and density, excellent
chemical resistance and low water absorption. The attractiveness of using porcelain has initiated intensive research work for
alternative raw materials because of the depletion and the high cost of the usual materials currently used in the ceramic
industry. In this research, the aim was to use boron-bearing solid wastes (Ca2B6O11.5H2O) as an alternative fluxing agent to
Na-feldspar (NaAlSi3O8) in fast-fired porcelain tile bodies produced under industrial conditions without altering the
microstructural, physical and chemical properties required from the final product. For this purpose, the suitability of the
colemanite-added porcelain tile bodies to fast-firing conditions was determined using an optical dilatometer. It was then
understood that a calcination process was needed in order to effectively use the waste in porcelain tile production. Therefore,
the calcination process was applied to the colemanite solid waste before the waste-added bodies were sintered at 1210℃ and
1130℃. The results were compared with those of the standard porcelain tile bodies produced at the same sintering
temperatures. After detailed phase analysis (XRD), microstructural examination (SEM-EDX) and physical-mechanical tests,
it was found that the standard porcelain tile body produced at 1210℃ (R1) could be obtained at 1130℃ by adding 5%
colemanite solid waste (by weight) to the standard tile body to replace Na-feldspar (R7). This result enables production of
porcelain tiles at lower temperatures without changing the other operational parameters, only using colemanite waste as a new
fluxing agent in the body formulations.
Porcelain tiles have become one of the most important products of the ceramic industry in the last decade mainly owing to
their attractive physical and mechanical properties including high strength, high fracture toughness and density, excellent
chemical resistance and low water absorption. The attractiveness of using porcelain has initiated intensive research work for
alternative raw materials because of the depletion and the high cost of the usual materials currently used in the ceramic
industry. In this research, the aim was to use boron-bearing solid wastes (Ca2B6O11.5H2O) as an alternative fluxing agent to
Na-feldspar (NaAlSi3O8) in fast-fired porcelain tile bodies produced under industrial conditions without altering the
microstructural, physical and chemical properties required from the final product. For this purpose, the suitability of the
colemanite-added porcelain tile bodies to fast-firing conditions was determined using an optical dilatometer. It was then
understood that a calcination process was needed in order to effectively use the waste in porcelain tile production. Therefore,
the calcination process was applied to the colemanite solid waste before the waste-added bodies were sintered at 1210℃ and
1130℃. The results were compared with those of the standard porcelain tile bodies produced at the same sintering
temperatures. After detailed phase analysis (XRD), microstructural examination (SEM-EDX) and physical-mechanical tests,
it was found that the standard porcelain tile body produced at 1210℃ (R1) could be obtained at 1130℃ by adding 5%
colemanite solid waste (by weight) to the standard tile body to replace Na-feldspar (R7). This result enables production of
porcelain tiles at lower temperatures without changing the other operational parameters, only using colemanite waste as a new
fluxing agent in the body formulations.
분석정보
연월일 | 이력구분 | 이력상세 | 등재구분 |
---|---|---|---|
2023 | 평가예정 | 해외DB학술지평가 신청대상 (해외등재 학술지 평가) | |
2022-10-24 | 학회명변경 | 한글명 : 세라믹연구소 -> 청정에너지연구소영문명 : Ceramic Research Institute -> Clean-Energy Research Institute | KCI등재 |
2020-01-01 | 평가 | 등재학술지 유지 (해외등재 학술지 평가) | KCI등재 |
2019-08-19 | 학회명변경 | 한글명 : 세라믹공정연구센터 -> 세라믹연구소영문명 : Ceramic Processing Research Center -> Ceramic Research Institute | KCI등재 |
2011-01-01 | 평가 | 등재학술지 유지 (등재유지) | KCI등재 |
2006-01-01 | 평가 | SCI 등재 (등재후보1차) | KCI등재 |
2003-01-01 | 평가 | 등재후보학술지 선정 (신규평가) | KCI후보 |
기준연도 | WOS-KCI 통합IF(2년) | KCIF(2년) | KCIF(3년) |
---|---|---|---|
2016 | 0 | 0 | 0 |
KCIF(4년) | KCIF(5년) | 중심성지수(3년) | 즉시성지수 |
0 | 0 | 0 | 0 |
서지정보 내보내기(Export)
닫기소장기관 정보
닫기권호소장정보
닫기오류접수
닫기오류 접수 확인
닫기음성서비스 신청
닫기음성서비스 신청 확인
닫기이용약관
닫기학술연구정보서비스 이용약관 (2017년 1월 1일 ~ 현재 적용)
학술연구정보서비스(이하 RISS)는 정보주체의 자유와 권리 보호를 위해 「개인정보 보호법」 및 관계 법령이 정한 바를 준수하여, 적법하게 개인정보를 처리하고 안전하게 관리하고 있습니다. 이에 「개인정보 보호법」 제30조에 따라 정보주체에게 개인정보 처리에 관한 절차 및 기준을 안내하고, 이와 관련한 고충을 신속하고 원활하게 처리할 수 있도록 하기 위하여 다음과 같이 개인정보 처리방침을 수립·공개합니다.
주요 개인정보 처리 표시(라벨링)
목 차
3년
또는 회원탈퇴시까지5년
(「전자상거래 등에서의 소비자보호에 관한3년
(「전자상거래 등에서의 소비자보호에 관한2년
이상(개인정보보호위원회 : 개인정보의 안전성 확보조치 기준)개인정보파일의 명칭 | 운영근거 / 처리목적 | 개인정보파일에 기록되는 개인정보의 항목 | 보유기간 | |
---|---|---|---|---|
학술연구정보서비스 이용자 가입정보 파일 | 한국교육학술정보원법 | 필수 | ID, 비밀번호, 성명, 생년월일, 신분(직업구분), 이메일, 소속분야, 웹진메일 수신동의 여부 | 3년 또는 탈퇴시 |
선택 | 소속기관명, 소속도서관명, 학과/부서명, 학번/직원번호, 휴대전화, 주소 |
구분 | 담당자 | 연락처 |
---|---|---|
KERIS 개인정보 보호책임자 | 정보보호본부 김태우 | - 이메일 : lsy@keris.or.kr - 전화번호 : 053-714-0439 - 팩스번호 : 053-714-0195 |
KERIS 개인정보 보호담당자 | 개인정보보호부 이상엽 | |
RISS 개인정보 보호책임자 | 대학학술본부 장금연 | - 이메일 : giltizen@keris.or.kr - 전화번호 : 053-714-0149 - 팩스번호 : 053-714-0194 |
RISS 개인정보 보호담당자 | 학술진흥부 길원진 |
자동로그아웃 안내
닫기인증오류 안내
닫기귀하께서는 휴면계정 전환 후 1년동안 회원정보 수집 및 이용에 대한
재동의를 하지 않으신 관계로 개인정보가 삭제되었습니다.
(참조 : RISS 이용약관 및 개인정보처리방침)
신규회원으로 가입하여 이용 부탁 드리며, 추가 문의는 고객센터로 연락 바랍니다.
- 기존 아이디 재사용 불가
휴면계정 안내
RISS는 [표준개인정보 보호지침]에 따라 2년을 주기로 개인정보 수집·이용에 관하여 (재)동의를 받고 있으며, (재)동의를 하지 않을 경우, 휴면계정으로 전환됩니다.
(※ 휴면계정은 원문이용 및 복사/대출 서비스를 이용할 수 없습니다.)
휴면계정으로 전환된 후 1년간 회원정보 수집·이용에 대한 재동의를 하지 않을 경우, RISS에서 자동탈퇴 및 개인정보가 삭제처리 됩니다.
고객센터 1599-3122
ARS번호+1번(회원가입 및 정보수정)