Diopside 금색 결정 유약의 발색 기구 = Optimum Condition and Color Mechanism for Gold Color Glaze in Diopside Crystallization

다국어 초록 (Multilingual Abstract)

Generally, the color gold has had a biased conception due to its traditional use. Thus, this bias has resulted in a lack of usage of golden glaze on ceramics and also a lack of extensive studies of such glazes. In this paper, optimum conditions and mechanism of formation of gold color crystallization glaze containing $Fe_2O_3$(hematite), which is developed for gold colors of ceramic glazes, were studied. Experimental result showed that there are pyroxene based on diopside and $TiO_2$ phase in the base of a crystallization glaze with a value of $TiO_2$ of 6 wt% confirmed by XRD and Raman Spectroscopy. When $Fe_2O_3$ was used as a colorant for the gold color, the $TiO_2$ peak became extinct and the intensity of the diopside peak was sharper. Feldspar of 60 wt%, talc of 20 wt% and limestone of 20 wt% were used as the starting materials and these were tested using a three component system. The best result of test was selected and extended to its vicinity as an experiment to determine $TiO_2$ and $Fe_2O_3$ contents. The glaze with $TiO_2$ of 6 wt% and $Fe_2O_3$ of 12 wt% addition showed stable pyroxene based diopside crystals and the development of gold color. This gold color was obtained with CIE-$L^*a^*b^*$ values of 51.27, 4.46, 16.15 (a grayish yellow brown color), which was gained using the following firing conditions: temperature increasing speed $5^{\circ}C$/min, holding for 1 h at $1280^{\circ}C$, annealing speed $3^{\circ}C$/min till $1100{\circ}C$, holding for 2 h at $1100{\circ}C$, and finally natural annealing.

참고문헌 (Reference)

• 1 M. V. Reddy, "α-Fe2O3 Nanoflakes as an Anode Material for Li-Ion Batteries" 17 : 2792-2799, 2007
• 2 L. Currie, "Stoneware Glazes - A Systematic Approach, 2nd." Bootstra press 128-131, 1986
• 3 H. C. Gogjow, "Science of Ceramic Glaze, 1st ed." Uchida Rokakuo Publishing Co. 311-312, 1994
• 4 F. J. Torres, "Pyroxene-based Glass-ceramic as Glazes for Floor Tiles" 25 : 349-355, 2005
• 5 I. N. Dvornichenko, "Production of Iron-containing Crystalline Glazes" 57 (57): 67-68, 2000
• 6 F. J. Torres, "Mechanism of Crystallization of Pyroxene-Based Glass-Ceramic as Glazes" 347 : 45-51, 2004
• 7 R. Casasola, "Glass- Ceramic Glazes for Ceramic Tiles: A Revew" 47 : 553-582, 2012
• 8 G. J. Redhammer, "Diopside(CaMgSi2O6)" 10 : 439-452, 1998
• 9 S. Y. Hwang, "A Study of Crystal Glaze" 27 : 419-442, 2004
• 10 P. D. LIU, "A Study of Ca-Mg Silicate Crystalline Glazes an Analysis on form of Crystals" 20 : 200-204, 2004