GC250D의 가스분위기 제어질화 공정에서 화합물층의 형성에 따른 표면조도의 변화 = Surface Roughness and Formation of Compound Layer in the Controlled Gaseous Nitriding Process on Cast Iron GC250D

다국어 초록 (Multilingual Abstract)

We investigated the changes in microstructure and surface roughness of the compound layer of GC250D gray cast iron, commonly used in brake discs, during gas nitriding. The gas atmosphere of the nitriding process was controlled with a hydrogen partial pressure of 49.5%, and the process was conducted at a nitriding temperature of 520oC with various process times. As the nitriding process time of the GC250D material increased, both the depth of hardening and the thickness of the compound layer increased, with a maximum surface hardness of approximately 1265 HV0.1 was measured. Additionally, the surface roughness increased with the process time. Phase analysis of the compound layer revealed an increase in the proportion of the γ′ phase as the nitriding process time increased. Changes in the formation of the compound layer were observed depending on the orientation of graphite within the material, leading to the formation of wedges. Therefore, the increase in surface roughness appears to be attributed to the uneven compounds, the expansion of the compound layer and wedges formed on the surface during the nitriding process.

참고문헌 (Reference)

• 1 C. P. Yeh, 50 : 2584-2592, 2009
• 2 A. Reis, 125 : 3777-3790, 2023
• 3 김용탁 ; 홍일민, 27 : 399-404, 2019
• 4 R. Sola, 9 : 11-16, 2008
• 5 한진, 7 : 19-24, 2015
• 6 E. Boztepe, 334 : 116-123, 2018
• 7 조영욱 ; 원종호 ; 우정호 ; 유상호 ; 조영래, 56 : 289-295, 2018
• 8 Y. W. Cho, 9 : 190-, 2019
• 9 Y. Xia, 2 : 78-82, 2007
• 10 P. Cornegia, 200 : 2391-2397, 2005
• 11 M. Yang, 22 : 1892-1898, 2013
• 12 K. M. Winter, 22 : 1945-1956, 2013
• 13 J. Baranowska, 100-101 : 271-275, 1998
• 14 R. O. Giacomelli, 314 : 18-27, 2017
• 15 E. Rolinski, 3/4 : 1-6, 2007
• 16 E. Rolinski, 18 : 1052-1059, 2009
• 17 F. Nishimura, 49-50, 2012
• 18 E. J. Mittermeijer, "Thermochemical Surface Engineering of Steels" Woodhead Publishing 313-553, 2015
• 19 E. Rolinski, "Encyclopedia of Iron, Steel, and Their Alloys" Taylor & Francis 3534-3550, 2018