Effect of intermetallic compound on the Al-Mg composite materials fabricated by mechanical ball milling and spark plasma sintering

다국어 초록 (Multilingual Abstract)

<P><B>Abstract</B></P> <P>We successfully prepared aluminum(Al)-magnesium(Mg) composite materials using a spark plasma sintering (SPS) process with pure Al and Mg powders as the raw materials. Composite materials containing 20, 50, or 80 vol% Mg (Al-20 vol% Mg, Al-50 vol% Mg, and Al-80 vol% Mg, respectively) were sintered at 410 °C and 50 MPa for 5 min. Using X-ray diffraction, intermetallic compounds such as Al<SUB>3</SUB>Mg<SUB>2</SUB> and Al<SUB>12</SUB>Mg<SUB>17</SUB> were detected, which were formed in the Al-Mg composite materials owing to the reaction between Al and Mg during SPS. The results of scanning electron microscopy with energy-dispersive spectroscopy and elemental mapping also confirmed the existence of the intermetallic compounds. The mechanical properties of the composite materials, analyzed using a Vickers hardness tester, showed that the Al-50 vol% Mg composite material exhibited the highest hardness value of approximately 189 HV. In conclusion, the composite materials manufactured with SPS may act as lightweight and high-efficiency materials, applicable in various fields, such as the aerospace and automobile industries.</P> <P><B>Highlights</B></P> <P> <UL> <LI> Al-Mg composite materials were fabricated using a spark plasma sintering process. </LI> <LI> The Al-50 vol% Mg composite material exhibited approximately 189 HV. </LI> <LI> Strengthening mechanism of Al-Mg composite materials is presented. </LI> <LI> These materials are expected to applicable as lightweight-multifunctional material. </LI> </UL> </P>