일정한 자장 하에서 증착된 Fe-Ni 박막에 대한 자기적 성질의 두께와 온도 의존성 = Thickness and Temperature Dependence of the Magnetic Properties for Fe-Ni Films Deposited in a Constant Magnetic Field

다국어 초록 (Multilingual Abstract)

The microstructure and the magnetic properties of Fe$_{100-x}$Ni$_{x}$ films
with thicknesses of 10 $\sim$ 100 nm deposited with using DC sputtering have been studied by using X--ray diffraction and
magnetic moment measurement. The samples are divided into two kinds of films those with and without an applied constant magnetic
field during preparation. The XRD patterns of the two kinds of Fe-Ni films show (111) and (200) planes as a strong preferred orientation.
The thickness dependence of the coercivity of the films was analyzed by using the Neel formula. In the films with an applied field during deposition,
an anomalous peak in the coercivity at a film thickness of 40 nm was observed, which could be explained by a change in the domain--wall
type at 40 nm. Also, the thickness and temperature dependences of the magnetization were fitted by applying the spin-wave theory.
From the fit, the exchange interaction constant between magnetic atoms in the samples was obtained.

국문 초록 (Abstract)

DC 스퍼터링에 의해서 증착된 10 $\sim$ 100 nm의 두께를 갖는 다결정
박막 Fe$_{100-x}$Ni$_{x}$의 미세구조와 자기적 성질을 X선 회절과
자기능률측정법에 의해서 연구하였다. 시료는 제작시 일정한 자기장을
인가해서 만든 것과 자기장을 인가하지 않은 것의 두 종류를
준비하였다. Fe-Ni박막에서 XRD 페턴은 두 종류의 시료 모두에서
(111)과 (200)면이 강한 우선 배양성을 보였다. 자기적 성질에서 가장
중요한 요소인 보자력과 포화자화를 증착조건에 따라 얼마나
민감한가를 조사 연구 하였다. 이 때 보자력의 두께의존성에 N\'{e}el
공식을 적용하였다. 그 결과 일정한 자장하에서 증착된 박막인 경우
박막두께 40 nm에서 비정상적인 큰 보자력값을 보였다. 이는 이
두께에서 자구벽형태의 천이가 나타남을 의미한다. 또한 포화자화의
두께와 온도의존성에 스핀파 이론을 적용하여 교환 상호작용의 상수
값을 구했다.