라텍스개질 콘크리트의 물-시멘트비에 따른 건조수축 특성 = Drying Shrinkage Properties of Latex Modified Concrete with Water-Cement Ratios

다국어 초록 (Multilingual Abstract)

Drying shrinkage cracking which may be caused by the relatively large specific suface is a matter of grave concern for latex modified concrete(LMC) overlay and rapid-setting cement latex modified concrete(RSLMC) overlay. LMC and RSLMC were studied for field applications very actively in terms of strength and durability in Korea. However, there were no considerations in drying shrinkage. Therefore, the purpose of this dissertation was to study the drying shrinkage properties of LMC and RSLMC with the main experimental variables such as cement types(ordinary portland cement, rapid setting cement), water-cement ratios and curing days at a same controlled environment of 60% of relative humidity and 20℃ of temperature. The drying shrinkage for specimens was measured with a digital dial gauge of Demec.
The test results showed that the drying shrinkage of LMC and RSLMC were considerably lower with low water-cement ratio, respectively. This might be attributed to the interlocking of hydrated cement and aggregates by a film of latex particles, water retention due to hydrophobic, and colloidal properties of the latexes resulting in reduced water evaporation.