Polymerization of dual cured composites by different thickness = 두께에 따른 이중 중합형 복합레진의 중합
저자
Kim, Yun Ju (Department of Conservative Dentistry, School of Dentistry, Kyungpook National University) ; Jin, Myoung Uk (Department of Conservative Dentistry, School of Dentistry, Kyungpook National University) ; Kim, Sung Kyo (Department of Conservative Dentistry, School of Dentistry, Kyungpook National University) ; Kwon, Tae-Yub (Department of Dental Biomaterials, School of Dentistry; Institute for Biomaterials Research & Development, Kyungpook National University) ; Kim, Young Kyung (Department of Conservative Dentistry, School of Dentistry, Kyungpook National University)
발행기관
학술지명
Restorative Dentistry & Endodontics(The Journal of Korean Academy of Conservative Dentistry)
권호사항
발행연도
2008
작성언어
English
주제어
KDC
515
등재정보
KCI등재
자료형태
학술저널
발행기관 URL
수록면
169-176(8쪽)
제공처
본 연구는 이중 중합형 복합레진에서 재료의 두께, 충전방법 및 중합방법에 따른 중합도를 미세경도 시험을 이용하여 측정하고자 하였다. 이중 중합형 복합레진으로는 MultiCore Flow (Ivovlar Vivadent AG, Schaan, Liechtenstein)와 Bis-Core (Bisco Inc., Schaumburg IL, USA)를 사용하였다. 시편의 제작은 각각 두께가 2 (단일충전), 4 (단일충전), 6 (단일충전과 적층충전), 8 (단일충전과 적층충전) ㎜의 Teflon mold에 재료를 주입한 다음 할로겐 광중합기 (Optilux 501, Kerr, Danbury, USA)를 사용하여 광중합하거나 암실에서 30분 동안 기다린 후(자가 중합) Teflon mold에서 제거하였다. 제거한 시편은 37℃ 증류수에 24시간 동안 보관한 후 각 시편의 윗면과 아랫면을 2000번 연마제와 PoGo system (Dentsply, Konstanz, Germany)을 이용하여 마무리하였다. Digital microhardness tester (FM-7, Future-Tech Corp., Tokyo, Japan)를 이용하여 경도값(Knoop hardness number)을 측정하였으며 윗면의 경도값/아랫면의 경도값을 이용하여 경도비를 계산하였다. 계측치는 one-way ANOVA로 통계 분석 후 사후검정은 Scheffe 다중비교법을 이용하였다.
이중 중합형 복합레진의 중합도에 대한 두께의 영향을 보면 재료에 따라 다른 결과를 보였다. 2, 4, 6 ㎜ 군에서는 MulriCore Flow와 Bis-Core 모두 두께에 의한 영향을 받지 않았지만 8 ㎜ 군에서는 MultiCore Flow의 아랫면에서 다른 두께의 군보다 낮은 경도값을 보였다.
충전방법에 따른 중합도의 차이를 보면, 재료의 두께나 재료에 따라 다른 결과를 보였다. 6 ㎜ 군에서는 단일충전군과 적층충전군 사이에 차이를 보이지 않았으나, 8 ㎜ 군에서는 Bis-Core에서는 차이가 없는 반면 MultiCore Flow에서 는 단일충전한 군이 적층충전한 군보다 낮은 경도비를 보였다.
중합방법에 따른 중합도의 차이를 보면, 재료에 따라 다른 결과를 보였다. Bis-Core의 경우에는 윗면과 아랫면 모두에서 이중 중합 시킨 군이 자가 중합 시킨 군보다 높은 경도값을 보였다. 그러나 MultiCore Flow의 경우, 윗면에서는 이중중합 시킨 군이 더 높은 경도간을 보였지만 아랫면에서는 더 낮은 값을 보였다.
따라서 본 연구의 결과에 따르면 코어용 이중 중합형 복합레진을 깊은 와동에 충전할 경우 적층충전이 추천되며, 또한 광중합을 해 줌으로써 더 좋은 물리적 성질을 기대할 수 있을 것으로 사료된다.
The purpose of this study was to evaluate the effect of thickness, filling methods and curing methods on the polymerization of dual cured core materials by means of microhardness test.
Two dual cured core materials, MultiCore Flow (Ivoclar Vivadent AG, Schaan, Liechtenstein) and Bis-Core (Bisco Inc., Schaumburg, IL, USA) were used in this study. 2 ㎜ (bulky filled), 4 ㎜ (bulky filled), 6 ㎜ (bulky and incrementally filled) and 8 ㎜ (bulky and incrementally filled)-thickness specimens were prepared with light cure or self cure mode. After storage at 37℃ for 24 hours, the Knoop hardness values (KHN) of top and bottom surfaces were measured and the microhardness ratio oftop and bottom surfaces was calculated. The data were analyzed using one-way ANOVA and Scheffe multiple comparison test, with α = 0.05.
The effect of thickness on the polymerization of dual cured composites showed material specific results. In 2, 4 and 6 ㎜ groups, the KHN of two materials were not affected by thickness. However, in 8 ㎜ group of MultiCore Flow, the KHN of the bottom surface was lower than those of other groups (p < 0.05). The effect of filling methods on the polymerization of dual cured composites was different by their thickness or materials. In 6 ㎜ thickness, there was no significant difference between bulk and incremental filling groups. In 8 ㎜ thickness, Bis-Core showed no significant difference between groups. However, in MultiCore Flow, the microhardness ratio of bulk filling group was lower than that of incremental filling group (p < 0.05). The effect of curing methods on the polymerization of dual cured composites showed material specific results. In Bis-Core, the KHN of dual cured group were higher than those of self cured group at both surfaces (p < 0.05). However, in MultiCore Flow, the results were not similar at both surfaces. At the top surface, dual cured group showed higher KHN than that of self cured group (p < 0.05). However, in the bottom surface, dual cured group showed lower value than that of self cured group (p < 0.05).
분석정보
서지정보 내보내기(Export)
닫기소장기관 정보
닫기권호소장정보
닫기오류접수
닫기오류 접수 확인
닫기음성서비스 신청
닫기음성서비스 신청 확인
닫기이용약관
닫기학술연구정보서비스 이용약관 (2017년 1월 1일 ~ 현재 적용)
학술연구정보서비스(이하 RISS)는 정보주체의 자유와 권리 보호를 위해 「개인정보 보호법」 및 관계 법령이 정한 바를 준수하여, 적법하게 개인정보를 처리하고 안전하게 관리하고 있습니다. 이에 「개인정보 보호법」 제30조에 따라 정보주체에게 개인정보 처리에 관한 절차 및 기준을 안내하고, 이와 관련한 고충을 신속하고 원활하게 처리할 수 있도록 하기 위하여 다음과 같이 개인정보 처리방침을 수립·공개합니다.
주요 개인정보 처리 표시(라벨링)
목 차
3년
또는 회원탈퇴시까지5년
(「전자상거래 등에서의 소비자보호에 관한3년
(「전자상거래 등에서의 소비자보호에 관한2년
이상(개인정보보호위원회 : 개인정보의 안전성 확보조치 기준)개인정보파일의 명칭 | 운영근거 / 처리목적 | 개인정보파일에 기록되는 개인정보의 항목 | 보유기간 | |
---|---|---|---|---|
학술연구정보서비스 이용자 가입정보 파일 | 한국교육학술정보원법 | 필수 | ID, 비밀번호, 성명, 생년월일, 신분(직업구분), 이메일, 소속분야, 웹진메일 수신동의 여부 | 3년 또는 탈퇴시 |
선택 | 소속기관명, 소속도서관명, 학과/부서명, 학번/직원번호, 휴대전화, 주소 |
구분 | 담당자 | 연락처 |
---|---|---|
KERIS 개인정보 보호책임자 | 정보보호본부 김태우 | - 이메일 : lsy@keris.or.kr - 전화번호 : 053-714-0439 - 팩스번호 : 053-714-0195 |
KERIS 개인정보 보호담당자 | 개인정보보호부 이상엽 | |
RISS 개인정보 보호책임자 | 대학학술본부 장금연 | - 이메일 : giltizen@keris.or.kr - 전화번호 : 053-714-0149 - 팩스번호 : 053-714-0194 |
RISS 개인정보 보호담당자 | 학술진흥부 길원진 |
자동로그아웃 안내
닫기인증오류 안내
닫기귀하께서는 휴면계정 전환 후 1년동안 회원정보 수집 및 이용에 대한
재동의를 하지 않으신 관계로 개인정보가 삭제되었습니다.
(참조 : RISS 이용약관 및 개인정보처리방침)
신규회원으로 가입하여 이용 부탁 드리며, 추가 문의는 고객센터로 연락 바랍니다.
- 기존 아이디 재사용 불가
휴면계정 안내
RISS는 [표준개인정보 보호지침]에 따라 2년을 주기로 개인정보 수집·이용에 관하여 (재)동의를 받고 있으며, (재)동의를 하지 않을 경우, 휴면계정으로 전환됩니다.
(※ 휴면계정은 원문이용 및 복사/대출 서비스를 이용할 수 없습니다.)
휴면계정으로 전환된 후 1년간 회원정보 수집·이용에 대한 재동의를 하지 않을 경우, RISS에서 자동탈퇴 및 개인정보가 삭제처리 됩니다.
고객센터 1599-3122
ARS번호+1번(회원가입 및 정보수정)