다국어 초록 (Multilingual Abstract)

Hardening mechanism associated with post-firing heat treatment of softening heat treated and then firing simulated Pd-Ag-Au alloy for bonding porcelain was examined by observing the change in hardness, crystal structure and microstructure. By post-firing heat treatment of as-cast, solution treated and pre-firing heat treated specimens at 650 ℃ after casting, the hardness value increased within 10 minutes. Then, hardness consistently increased until 30 minutes, and gap of hardness value among the specimens was reduced. The increase in hardness after post-firing heat treatment was caused by grain interior precipitation in the matrix. The softening heat treatment did not affect the increase in hardness by post-firing heat treatment. The precipitated phase from the parent Pd-Ag-Au-rich α phase with face-centered cubic structure by post-firing heat treatment was Pd3(Sn, In) phase with face-centered tetragonal structure, which has lattice parameters of a<SUB>200</SUB>=4.0907 Å, c<SUB>002</SUB>=3.745 Å. From above results, appropriate post-firing heat treatment in order to support the hardness of Pd-Ag-Au metal substructure was expected to bring positive effects to durability of the prosthesis.

목차 (Table of Contents)

• Abstract
• Ⅰ. INTRODUCTION
• Ⅱ. MATERIALS AND METHODS
• Ⅲ. RESULTS
• IV. DISCUSSION
• Ⅵ. REFERENCES

참고문헌 (Reference)

• 1 Yamamoto M, "The metal ceramics" Quintessence 1982
• 2 Li D, "Study of Pd-Ag dental alloys : examination of effect of casting porosity on fatigue behavior and microstructural analysis" 21 : 2723-2731, 2010
• 3 Liu WB, "Strengthening of a Pd-free high gold dental alloy for porcelain bonding by a pre-firing heat treatment" 23 : 1136-1141, 2007
• 4 Anusavice KJ, "Phillips'science of dental materials" 377-384, 2013
• 5 Yu CH, "Phase transformation and Microstructural changes during ageing process of an Ag-Pd-Cu-Au alloy" 460 : 331-336, 2008
• 6 Vermilyea SG, "Metallurgical structure and microhardness of four new palladium-based alloys" 5 : 288-294, 1996
• 7 Mezger PR, "Metallurgical aspects of palladium-silver porcelain-bonding alloys" 17 : 90-93, 1989
• 8 Bryant RA, "Measurement of distortion in fixed partial dentures resulting from degassing" 42 : 515-520, 1979
• 9 Fischer J, "Improving the processing of high-gold metal-ceramic frameworks by a pre-firing heat treatment" 16 : 109-113, 2000
• 10 German RM, "Hardening reactions in a high-gold content ceramo-metal alloy" 59 : 1960-1965, 1980
• 11 Kim HI, "Hardening and overaging mechanism of a commercial Au-Ag-Cu-Pd dental alloy" 441 : 124-130, 2007
• 12 Koike K, "Fabrication of ceramo-metal crowns with accurate fitness : deformation of casting and its remedies" 5 : 31-41, 1997
• 13 Culity BD, "Elements of X-ray diffraction" Addison-Wesley publishing Co., Inc 506-507, 1978
• 14 Cambell SD, "Effect of firing cycle and surface finishing on distortion of metal ceramic casting" 74 : 476-481, 1995
• 15 Tuccillo JJ, "Creep and sag properties of a porcelain-gold alloy" 46 : 579-583, 1967
• 16 Hisatsune K, "Age-hardening behavior in a palladium-base dental porcelain fused alloy" 25 : 177-184, 1990
• 17 Seol HJ, "Age-hardening and related phase transformation in an experimenta Ag-Cu-Pd-Au alloy" 407 : 182-187, 2006